美国杜邦授权塑胶原材料中国上海代理商

长期稳定销售系列型号：

PA66 101 NC010

PA66 101F BKB009

PA66 101F NC010

PA66 101L BKB080

PA66 101L NC010

PA66 FG101L NC010

PA66 101L BKB009

PA66 103FHS BKB009

PA66 103FHS NC010

PA66 103HSL BKB080

PA66 103FHS BKB038

PA66 103FHSA NC010

PA66 MT409AHS BK010

PA66 MT409AHS NC010

PA66 ST801A NC010A

PA66 ST801AHS BK010

PA66 ST801AHS NC010

PA66 ST801AW BK195

PA66 ST801AW NC010

PA66 FG408L NC010

PA66 ST801 NC010A

PA66 444AHS BK152

PA66 70G13L NC010

PA66 70G13HS1L NC010

PA66 70G13HS1L BK031

PA66 BM70G15HSLR BK537

PA66 BM70G20HSLX BK537

PA66 70G20HSL NC010

PA66 70G25HSL NC010

PA66 70G25HSLR NC010

PA66 70G25HSLR BK099

PA66 70G30L NC010

PA66 70G30HSL NC010

PA66 70G30HSL BK039B

PA66 70G30HSLR NC010

PA66 70G30HSLR BK099

PA66 FG70G30HSLR NC010

PA66 70G33L NC010

PA66 70G33L BK031

PA66 70G33HS1L NC010

PA66 70G33HS1L BK031

PA66 70G35EF NC010

PA66 70G35HSL NC010

PA66 70G35HSL BK039B

PA66 70G35HSLX BK357

PA66 70G35HSRX BK099

PA66 70G35HSLRA4 BK267

PA66 LM70G35HSLX BK314

PA66 70G43L NC010

PA66 70G43HSLA BK099

美国杜邦尼龙66 Zytel PA66 注射成型工艺

干燥处理:玻璃纤维增强 Zytel 尼龙66在成型加工之前必须进行干燥.未增强尼龙66树脂的干燥方法适用于玻璃纤维增强尼龙“的干燥。玻璃纤维增强尼龙“的回料,在成型之前也要进行干燥处理。GRZ尼龙68的水分含量要求小于0.2%,如基露在大于50%RH的环境中需干燥1~2H

料简温度:料筒后部温度高达299℃,原因是为了改善螺杆后退速度,减少玻纤的损坏,以及减少由于未熔融颗粒与螺杆或料筒之间所产生的磨损。料筒后部温度高不会发生架桥,可使落料正常。同时较高的温度也减少了螺杆的扭矩负荷,当在快速成型时也减少了螺杆的失速和损坏。

喷嘴温度:成型玻璃纤维增强 尼龙66,喷嘴温度在260~277℃之间,然而在冷模时,喷嘴温度必须提高,以防止喷嘴过早的冻结.

模具温度:模具温度在宽广的范围内,玻璃纤维增强尼龙“都可似成型,但为了获得良好的制品外观质量,使熔料更好地充填模腔,模具**加热,一般在99~121℃之间。另外不必耽心因较高的模温而增加成型周期.因为玻璃纤维增强尼龙66凝固迅速,在高模温环境中仍保持刚性,所以制品从热模内很容易顶出而不会变形。为了控制制品尺寸,尤其是多模腔制品,模腔具有均匀的表面温度是一个必要的条件。

成型周期:玻璃纤维增强尼龙66的成型周期通常比未增强尼龙66树脂短约10~30%,玻璃纤维增强尼龙66的成型周期与制品壁厚的关系。

注射速度:玻璃纤维增强尼龙66比未增强尼龙“凝固更快,必须使用快速注射.制品表面光洁度欠佳(起霜〕,通常是过早凝固造成的,但往往被错认为是玻纤分散不良或树脂潮湿所引起的。,各种制品壁厚在冻结之前所需的**少注射时间。

注射压力:玻璃纤维增强尼龙“的熔体粘度较高,所需的注射压力比未增强尼龙66树脂大.注射压力的大小视制品形状、浇口、模具温度等而定。

背压:成型玻璃纤维增强尼龙66不使用背压,背压有可能引起纤维的损坏,并引起制品某些物理机械性能降低。

脱模:玻璃纤维增强尼龙66比未增强尼龙66具有更好的脱模特性。但当增强回料与新料棍合使用时,个别产品需使用0.05~0.10男二硬脂酸铝(脱模剂),以便顺利顶出制品。